For inventory control purposes product name may be followed by an X.

Products labeled FEP CJ 99 and FEP CJ 99 X are equivalent and all information in this document is applicable to both.

Typical Application
Wire and cable insulation, small tubing and injection molded parts.

DuPont Teflon ® FEP CJ 99 is a melt-processible copolymer of tetrafluoroethylene and hexafluoropropylene without additives that meets the requirements of ASTM D 2116 type I.

Thanks to the unique combination of a Melt Flow Rate in the range of 9 g/10 min and MIT flexlife above 40 000 cycles, this resin offers both attractive processing speeds and high stress-rack resistance in addition to the excellent characteristics typical of Teflon ® fluoropolymer resins, such as non-ageing characteristics, chemical inertness, exceptional electrical properties, low flammability, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption and excellent weather resistance. The increased transparency of Teflon ® FEP CJ 99 will also allow better colourability.

Stress crack resistance is an important element in establishing end-use performance. Extensive testing of wire and cable constructions is required for definitive performance evaluation. Well-known and most comprehensive tests for stress rack resistance of wire and cable are mandrel wrap tests as described in the military specification MIL-W-22759 (aerospace) and ISO 6722/LV112 (automotive). Experience has shown that the MIT folding endurance or flex life test, based on ASTM D 2176, performed on a thin film of resin, gives a good correlation with stress crack resistance. Resins with a higher MIT flex life, perform better in the stress-crack resistance tests. Teflon ® FEP CJ 99 has a higher degree of stress crack resistance than most FEP resins with similar viscosity (MFR) and offers higher productivity than FEP resins with similar stress crack resistance (MIT). We recommend that for applications involving repeated thermal and flex cycling, specific tests on the final cable always should be undertaken. The MIT test results should be viewed as guide to comparative performance of the various grades of resin.

材料状态 

供货地区 

特性 

用途 

机构评级 

形式 

加工方法 

额定值

单位制

测试方法

g/10 min

%

额定值

单位制

测试方法

psi

%

额定值

单位制

测试方法

额定值

单位制

测试方法

额定值

单位制

测试方法

°F

°F

额定值

单位制

测试方法

V/mil

V/mil

额定值

单位制

测试方法

%

额定值

单位制

测试方法

sec^-1

Cycles

特性 may also be described by the following terms: 良好的耐化学品性，耐化学品性良好, 良好的柔性，柔软的, 低摩擦系数, 韧性良好，不易磨损, High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, 良好的耐候性，耐候性的, **，**循环, Good Electrical Properties, 良好的着色性.

用途 may also be described by the following terms: 电线电缆应用，电线电缆用途.