Mobil Aviation Grease SHC 100
Synthetic Aviation Grease
Product Description
Mobil Aviation Grease SHC 100 is a supreme performance synthetic grease which combines the unique features of a polyalphaolefin (PAO) synthetic base fluid with those of a high quality lithium complex soap thickener. The thickener system provides a high dropping point, excellent resistance to water wash, and a tenacious structural stability. The unique physical properties of the synthetic base oil, combined with seleced additives, provide outstanding protection against wear, rust, corrosion, and high temperature degradation. The wax-free feature of the synthetic base oil allows for low-temperature mobility/pumpability and low starting and running torque values. Mobil Aviation Grease SHC 100 is the product of choice for aircraft wheel bearing applications.
Features and Benefits
A key factor in the development of Mobil Aviation Grease SHC 100 was the close contact between ExxonMobil product engineers and key OEMs to ensure that the lubricant would provide exceptional performance in aircraft wheel bearings. This work has helped to /confirm/i the results from ExxonMobil laboratory tests showing the exceptional performance of Mobil Aviation Grease SHC 100 including long grease life, enhanced bearing protection and bearing life in aircraft wheels, and wide temperature range of application.
To combat high thermal exposure of the oil, ExxonMobil product formulators chose synthetic hydrocarbon base oils for Mobil Aviation Grease SHC 100 because of their exceptional thermal/oxidative resistance potential. A state-of-the-art lithium complex thickener technology was developed and used specific additives to enhance performance.
Mobil Aviation Grease SHC 100 offers the following features and benefits:
Features |
Advantages and Potential Benefits |
High viscosity index (VI) base stock with no wax content |
Wide application temperature ranges, with excellent protection at high temperatures and low torque, easy start-up at low temperatures. |
Outstanding high temperature and low temperature performance |
Thicker fluid films protecting against wear of equipment parts operating at high temperature |
Excellent protection against wear, rust, and corrosion |
Reduced downtime and maintenance costs because of reduced replacement of equipment parts |
Excellent structural stability and oxidation resistance |
Long intervals between re-lubrication and improved bearing life |
Outstanding structural stability in the presence of water |
Excellent grease retention on parts in hostile wet environments |
Low volatility |
Little loss of lubricating oil |
Applications
Mobil Aviation Grease SHC 100 is recommended for aviation applications which need a lubricant that can perform normal functions, yet go far beyond in terms of high and low temperatures and long-life performance. It is a NLGI Grade 2/ISO VG 100 grease having the cold-temperature pumping resistance of most mineral-oil NLGI Grade 0 greases. It provides outstanding protection at operating temperatures from –54 ?C (-65 ?F) to 177 ?C (350 ?F).
Mobil Aviation grease SHC 100 is recommended for high speed, heavy load applications such as wheel bearings, as well as for slower speed, high load applications such as landing gear bearings, slides, and joints.
Mobil Aviation Grease SHC 100 is approved as a wheel bearing grease by all major aircraft wheel manufacturers.
Specifications and Approvals
Mobil Aviation Grease SHC 100 |
Approved as a wheel bearing grease |
ABSC (Meggitt) |
X |
Dunlop (Meggitt) |
X |
Goodrich |
X |
Honeywell (formerly AlliedSignal) |
X |
Messier-Bugatti |
X |
Parker-Cleveland |
X |
Typical Properties
|
Test Method |
Mobil Aviation Grease SHC 100 (1) |
Spec Limit |
NLGI Grade |
|
2 |
|
Soap Type |
|
Lithium Complex |
|
Structure |
Visual |
Smooth; Slight Tack |
|
Color |
Visual |
Red |
|
base Oil Viscosity, cSt |
ASTM D 445 |
|
|
at 40 ?C |
|
100 |
|
at 100 ?C |
|
14.5 |
|
Penetration at 25?C (77?F), 60 Stroke Worked, mm/10 |
ASTM D 217 |
280 |
255 - 300 |
Extended Worked Stability, 100,000 strokes |
FTM 313 |
313 |
350 max |
Dropping Point, ?C (?F) |
ASTM D 2265 |
278 (532) |
246 (475) min |
Copper Strip Corrosion, 24 Hrs at 100?C |
ASTM D 4048 |
Pass |
1b max |
Four-Ball Wear, Scar dia, mm |
ASTM D 2266 |
0.5 |
0.8 max |
Four-Ball EP, Weld Load, kgf |
ASTM D 2596 |
250 |
|
Four-ball EP, Load Wear Index, kgf |
ASTM D 2596 |
40 |
|
Water Washout, wt % |
ASTM D 1264 |
|
|
1 Hr at 79?C (175?F) |
|
7 |
|
1 Hr at 41?C (105?F) |
|
3 |
20 max |
Rust Protection, 48 Hrs at 125?F, ?1mm dia Corrosion Spots |
ASTM D 1743 |
Pass |
0 in 2 out of 3 bearings |
Bomb Oxidation, pressure drop in psi |
ASTM D 942 |
|
|
100 hr at 99?C (210?F) |
|
3 |
|
500 hr at 99?C (210?F) |
|
5 |
|
Oil Separation, 30 Hrs at 177?C, wt % |
ASTM D 6184 |
7 |
12 max |
Evaporation, 30 Hrs at 177?C, wt % |
ASTM D 972 |
5 |
|
Dirt Count, Particles/mL |
FTM 3005 |
|
|
25-125 Micron |
|
Pass |
1000 Max |
Larger than 125 Micron |
|
Pass |
0 |
Low Temp. Torque @ -54?C (-65?F), Nm (g-cm) |
ASTM D 1478 |
|
|
Starting |
|
0.3 (3100) |
2.0 (20400) |
Running |
|
0.1 (1020) |
0.5 (5100) |
(1) Values may vary within modest ranges |
|
|
|