General | ||||
Material Status
|
|
|||
Literature 1
|
|
|||
Search for UL Yellow Card
|
|
|||
Availability
|
|
|||
Additive
|
|
|||
Features
|
|
|||
Processing Method
|
|
|||
Resin ID (ISO 1043)
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.26
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
2.0
|
--
|
%
|
|
Flow
|
2.0
|
--
|
%
|
|
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
11
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
3.2
|
--
|
%
|
|
Viscosity Number
|
190
|
--
|
cm³/g
|
ISO 307 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
ISO 527-2 | |||
--
|
3100
|
900
|
MPa
|
|
120°C
|
775
|
--
|
MPa
|
|
160°C
|
650
|
--
|
MPa
|
|
180°C
|
600
|
--
|
MPa
|
|
200°C
|
560
|
--
|
MPa
|
|
Tensile Stress
|
ISO 527-2 | |||
Yield, 120°C
|
45.0
|
--
|
MPa
|
|
Yield, 160°C
|
40.0
|
--
|
MPa
|
|
Yield, 180°C
|
35.0
|
--
|
MPa
|
|
Yield, 200°C
|
30.0
|
--
|
MPa
|
|
Break
|
90.0
|
60.0
|
MPa
|
|
Tensile Strain (Break)
|
20
|
> 50
|
%
|
ISO 527-2 |
Nominal Tensile Strain at Break
|
ISO 527-2 | |||
180°C
|
> 50
|
--
|
%
|
|
200°C
|
> 50
|
--
|
%
|
|
Flexural Modulus
|
2900
|
--
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength (23°C)
|
9.0
|
--
|
kJ/m²
|
ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C)
|
No Break
|
--
|
ISO 179/1eU | |
Notched Izod Impact Strength (23°C)
|
8.5
|
--
|
kJ/m²
|
ISO 180/1A |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
290
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
190
|
--
|
°C
|
ISO 75-2/A |
Glass Transition Temperature 2
|
75.0
|
--
|
°C
|
ISO 11357-2 |
Vicat Softening Temperature
|
290
|
--
|
°C
|
ISO 306/B50 |
Melting Temperature 2
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
ISO 11359-2 | |||
Flow
|
8.5E-5
|
--
|
cm/cm/°C
|
|
Transverse
|
1.1E-4
|
--
|
cm/cm/°C
|
|
Thermal Index - 5000 hr
|
152
|
--
|
°C
|
IEC 60216 |
Injection |
Dry
|
Unit
|
|
Drying Temperature - Desiccant Dryer
|
80 to 110
|
°C
|
|
Rear Temperature
|
290 to 315
|
°C
|
|
Middle Temperature
|
295 to 315
|
°C
|
|
Front Temperature
|
300 to 315
|
°C
|
|
Nozzle Temperature
|
295 to 315
|
°C
|
|
Processing (Melt) Temp
|
300 to 315
|
°C
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
Injection Rate
|
Slow-Moderate
|
||
Back Pressure
|
1.00 to 5.00
|
MPa
|
|
Screw Compression Ratio
|
2.5:1.0
|