General | ||||
Material Status
|
|
|||
Literature 1
|
|
|||
Search for UL Yellow Card
|
|
|||
Availability
|
|
|||
Additive
|
|
|||
Features
|
|
|||
Resin ID (ISO 1043)
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.18
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.4
|
--
|
%
|
|
Flow
|
1.4
|
--
|
%
|
|
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
13
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
3.2
|
--
|
%
|
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
ISO 527-2 | |||
--
|
3700
|
1200
|
MPa
|
|
120°C
|
1100
|
--
|
MPa
|
|
160°C
|
950
|
--
|
MPa
|
|
180°C
|
900
|
--
|
MPa
|
|
200°C
|
800
|
--
|
MPa
|
|
Tensile Stress
|
ISO 527-2 | |||
Yield, 120°C
|
50.0
|
--
|
MPa
|
|
Yield, 160°C
|
40.0
|
--
|
MPa
|
|
Yield, 180°C
|
40.0
|
--
|
MPa
|
|
Yield, 200°C
|
35.0
|
--
|
MPa
|
|
Break
|
100
|
55.0
|
MPa
|
|
Nominal Tensile Strain at Break
|
ISO 527-2 | |||
--
|
6.0
|
30
|
%
|
|
180°C
|
> 50
|
--
|
%
|
|
200°C
|
> 50
|
--
|
%
|
|
Flexural Modulus
|
ISO 178 | |||
--
|
3200
|
1000
|
MPa
|
|
120°C
|
1100
|
--
|
MPa
|
|
160°C
|
850
|
--
|
MPa
|
|
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
3.0
|
2.5
|
kJ/m²
|
|
23°C
|
5.0
|
15
|
kJ/m²
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Melting Temperature 2
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
ISO 11359-2 | |||
Flow
|
8.0E-5
|
--
|
cm/cm/°C
|
|
Transverse
|
7.0E-5
|
--
|
cm/cm/°C
|
Injection |
Dry
|
Unit
|
|
Drying Temperature
|
80
|
°C
|
|
Drying Time
|
2.0
|
hr
|
|
Rear Temperature
|
280 to 320
|
°C
|
|
Middle Temperature
|
300 to 320
|
°C
|
|
Front Temperature
|
300 to 320
|
°C
|
|
Nozzle Temperature
|
300 to 320
|
°C
|
|
Processing (Melt) Temp
|
310 to 320
|
°C
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
Injection Rate
|
Moderate-Fast
|
||
Back Pressure
|
2.00 to 10.0
|
MPa
|
|
Screw Compression Ratio
|
2.5:1.0
|