General | ||||
Material Status
|
|
|||
Literature 1
|
|
|||
Search for UL Yellow Card
|
|
|||
Availability
|
|
|||
Filler / Reinforcement
|
|
|||
Additive
|
|
|||
Features
|
|
|||
Uses
|
|
|||
Processing Method
|
|
|||
Resin ID (ISO 1043)
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.49
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.1
|
--
|
%
|
|
Flow
|
0.40
|
--
|
%
|
|
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
6.3
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
2.3
|
--
|
%
|
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
11500
|
8000
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
145
|
100
|
MPa
|
ISO 527-2 |
Tensile Strain (Break)
|
2.1
|
3.1
|
%
|
ISO 527-2 |
Flexural Modulus
|
10500
|
8000
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength (23°C)
|
9.0
|
10
|
kJ/m²
|
ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C)
|
50
|
60
|
kJ/m²
|
ISO 179/1eU |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
285
|
--
|
°C
|
ISO 75-2/A |
Glass Transition Temperature 2
|
75.0
|
--
|
°C
|
ISO 11357-2 |
Melting Temperature 2
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
||||
Flow
|
3.0E-5
|
--
|
cm/cm/°C
|
ASTM D696 |
Flow
|
1.7E-5
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Transverse
|
4.0E-5
|
--
|
cm/cm/°C
|
ASTM D696 |
Transverse
|
7.0E-5
|
--
|
cm/cm/°C
|
ISO 11359-2 |
RTI Elec (0.180 mm)
|
120
|
--
|
°C
|
UL 746 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity
|
> 1.0E+15
|
1.0E+13
|
ohms·cm
|
IEC 60093 |
Electric Strength
|
30
|
24
|
kV/mm
|
IEC 60243-1 |
Relative Permittivity
|
IEC 60250 | |||
100 Hz
|
4.40
|
11.0
|
||
1 MHz
|
4.10
|
5.00
|
||
1.00 GHz
|
3.90
|
4.10
|
||
10.0 GHz
|
3.80
|
4.00
|
||
Dissipation Factor
|
IEC 60250 | |||
100 Hz
|
7.2E-3
|
0.21
|
||
1 MHz
|
0.017
|
0.10
|
||
Comparative Tracking Index
|
550
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
0.180 mm
|
V-0
|
--
|
||
1.5 mm
|
V-0
|
--
|
||
Oxygen Index
|
48
|
--
|
%
|
ISO 4589-2 |
Injection |
Dry
|
Unit
|
|
Drying Temperature
|
100
|
°C
|
|
Drying Time
|
4.0 to 8.0
|
hr
|
|
Rear Temperature
|
300 to 310
|
°C
|
|
Middle Temperature
|
305 to 315
|
°C
|
|
Front Temperature
|
310 to 320
|
°C
|
|
Nozzle Temperature
|
315 to 325
|
°C
|
|
Processing (Melt) Temp
|
320 to 330
|
°C
|
|
Mold Temperature
|
100 to 120
|
°C
|
|
Injection Rate
|
Moderate-Fast
|
||
Back Pressure
|
0.500 to 3.00
|
MPa
|
|
Screw Compression Ratio
|
2.5:1.0
|