Stanyl® 46SF5030
General |
|
Material Status
|
|
Literature 1
|
- Technical Datasheet (English)
|
UL Yellow Card 2
|
|
Search for UL Yellow Card
|
|
Availability
|
|
Filler / Reinforcement
|
- Glass Fiber, 30% Filler by Weight
|
Additive
|
|
Features
|
|
Processing Method
|
|
Resin ID (ISO 1043)
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.68
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
|
|
|
ISO 294-4 |
Across Flow
|
1.1
|
--
|
%
|
|
Flow
|
0.40
|
--
|
%
|
|
Water Absorption
|
|
|
|
ISO 62 |
Saturation, 23°C
|
5.8
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
1.6
|
--
|
%
|
|
Viscosity Number
|
66.0
|
--
|
cm³/g
|
ISO 307 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
12000
|
7500
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
170
|
110
|
MPa
|
ISO 527-2 |
Tensile Strain (Break)
|
1.9
|
2.8
|
%
|
ISO 527-2 |
Flexural Modulus
|
11000
|
6800
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
|
|
|
ISO 179/1eA |
-30°C
|
12
|
12
|
kJ/m²
|
|
23°C
|
13
|
13
|
kJ/m²
|
|
Charpy Unnotched Impact Strength (23°C)
|
40
|
40
|
kJ/m²
|
ISO 179/1eU |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature
|
|
|
|
|
0.45 MPa, Unannealed
|
290
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
290
|
--
|
°C
|
ISO 75-2/A |
Glass Transition Temperature 3
|
75.0
|
--
|
°C
|
ISO 11357-2 |
Vicat Softening Temperature
|
290
|
--
|
°C
|
ISO 306/B50 |
Melting Temperature 3
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
|
|
|
ISO 11359-2 |
Flow
|
2.0E-5
|
--
|
cm/cm/°C
|
|
Transverse
|
4.5E-5
|
--
|
cm/cm/°C
|
|
RTI Elec (0.35 mm)
|
65.0
|
--
|
°C
|
UL 746 |
Effective Thermal Diffusivity
|
1.01E-7
|
--
|
m²/s
|
|
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity
|
> 1.0E+15
|
1.0E+10
|
ohms·cm
|
IEC 60093 |
Electric Strength
|
30
|
20
|
kV/mm
|
IEC 60243-1 |
Relative Permittivity
|
|
|
|
IEC 60250 |
100 Hz
|
4.30
|
--
|
|
|
1 MHz
|
4.00
|
--
|
|
|
Dissipation Factor
|
|
|
|
IEC 60250 |
100 Hz
|
6.0E-3
|
--
|
|
|
1 MHz
|
0.016
|
--
|
|
|
Comparative Tracking Index
|
225
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flammability Classification
|
|
|
|
IEC 60695-11-10, -20 |
0.35 mm
|
V-0
|
--
|
|
|
1.5 mm
|
V-0
|
--
|
|
|
Fill Analysis |
Dry
|
Conditioned
|
Unit
|
|
Melt Density
|
1.45
|
--
|
g/cm³
|
|
Melt Thermal Conductivity
|
0.26
|
--
|
W/m/K
|
|
Specific Heat Capacity of Melt
|
1750
|
--
|
J/kg/°C
|
|
Injection |
Dry
|
Unit
|
|
Drying Temperature
|
80
|
°C
|
|
Drying Time
|
4.0 to 8.0
|
hr
|
|
Rear Temperature
|
280 to 310
|
°C
|
|
Middle Temperature
|
300 to 315
|
°C
|
|
Front Temperature
|
300 to 315
|
°C
|
|
Nozzle Temperature
|
300 to 310
|
°C
|
|
Processing (Melt) Temp
|
310 to 320
|
°C
|
|
Mold Temperature
|
60 to 120
|
°C
|
|
Injection Rate
|
Moderate-Fast
|
|
|
Back Pressure
|
1.00
|
MPa
|
|
Screw Compression Ratio
|
2.5:1.0
|
|
|
|
|
|