TYPICAL PROPERTIES (1) |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 2.0 in/min |
8400 |
psi |
ASTM D 638 |
Tensile Stress, brk, Type I, 2.0 in/min |
8200 |
psi |
ASTM D 638 |
Tensile Strain, yld, Type I, 2.0 in/min |
5.7 |
% |
ASTM D 638 |
Tensile Strain, brk, Type I, 2.0 in/min |
117.9 |
% |
ASTM D 638 |
Tensile Modulus, 2.0 in/min |
328000 |
psi |
ASTM D 638 |
Flexural Stress, yld, 0.05 in/min, 2 in span |
13700 |
psi |
ASTM D 790 |
Flexural Modulus, 0.05 in/min, 2 in span |
326000 |
psi |
ASTM D 790 |
Tensile Stress, yield, 50 mm/min |
57 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
56 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
5.4 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
119.4 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2340 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
89 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2140 |
MPa |
ISO 178 |
Hardness, Rockwell L |
89 |
- |
ISO 2039-2 |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, notched, 73°F |
13.7 |
ft-lb/in |
ASTM D 256 |
Izod Impact, notched, -22°F |
11.5 |
ft-lb/in |
ASTM D 256 |
Instrumented Impact Total Energy, 73°F |
662 |
in-lb |
ASTM D 3763 |
Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C |
65 |
kJ/m² |
ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C |
55 |
kJ/m² |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
65 |
kJ/m² |
ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
45 |
kJ/m² |
ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp, Rate A/50 |
281 |
°F |
ASTM D 1525 |
HDT, 264 psi, 0.125 in, unannealed |
251 |
°F |
ASTM D 648 |
CTE, flow, -40°F to 200°F |
4.15E-05 |
1/°F |
ASTM E 831 |
CTE, xflow, -40°F to 200°F |
4.24E-05 |
1/°F |
ASTM E 831 |
CTE, 23°C to 80°C, flow |
7.48E-05 |
1/°C |
ISO 11359-2 |
CTE, 23°C to 80°C, xflow |
7.64E-05 |
1/°C |
ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C |
pass |
- |
IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 |
138 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
139 |
°C |
ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
116 |
°C |
ISO 75/Af |
Relative Temp Index, Elec |
130 |
°C |
UL 746B |
Relative Temp Index, Mech w/o impact |
130 |
°C |
UL 746B |
PHYSICAL |
Value |
Unit |
Standard |
Specific Gravity |
1.19 |
- |
ASTM D 792 |
Mold Shrinkage, flow, 0.125" (5) |
0.4 - 0.8 |
% |
SABIC Method |
Mold Shrinkage, xflow, 0.125" (5) |
0.4 - 0.8 |
% |
SABIC Method |
Melt Flow Rate, 300°C/1.2 kgf |
20 |
g/10 min |
ASTM D 1238 |
Density |
0.04 |
lb/in³ |
ISO 1183 |
Water Absorption, equilibrium, 73°F |
0.12 |
% |
ISO 62 |
Moisture Absorption (23°C / 50% RH) |
0.09 |
% |
ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg |
19 |
cm³/10 min |
ISO 1133 |
OPTICAL |
Value |
Unit |
Standard |
Light Transmission, 0.1 in |
82 |
% |
ASTM D 1003 |
Haze, 0.1 in |
3 |
% |
ASTM D 1003 |
ELECTRICAL |
Value |
Unit |
Standard |
Volume Resistivity |
>1.E+15 |
Ohm-cm |
ASTM D 257 |
Surface Resistivity |
>1.E+15 |
Ohm |
ASTM D 257 |
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
UL Recognized, 94HB Flame Class Rating (3) |
0.059 |
in |
UL 94 |
Glow Wire Flammability Index 960°C, passes at |
0.118 |
in |
IEC 60695-2-12 |
Glow Wire Ignitability Temperature, 0.8 mm |
850 |
°C |
IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 3.0 mm |
850 |
°C |
IEC 60695-2-13 |