LEXAN ™ Resin EXL1036 |
Europe-Africa-Middle East: LIMITED USE |
LEXAN EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good hiding power as caplayer in combination with excellent extrusion processing characteristics. LEXAN EXL1036 resin is available in limited opaque colors only and is an excellent candidate for a broad range of (co-)extrusion/thermoforming applications. |
Property |
TYPICAL PROPERTIES (1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 590 | kgf/cm² | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 660 | kgf/cm² | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 130 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 21600 | kgf/cm² | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 890 | kgf/cm² | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 21400 | kgf/cm² | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 57 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 66 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2070 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 1960 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23°C | 83 | cm-kgf/cm | ASTM D 256 | |
Izod Impact, notched, -30°C | 69 | cm-kgf/cm | ASTM D 256 | |
Instrumented Impact Total Energy, 23°C | 530 | cm-kgf | ASTM D 3763 | |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U | |
Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A | |
Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 143 | °C | ASTM D 1525 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D 648 | |
CTE, -40°C to 40°C, flow | 6.66E-05 | 1/°C | ASTM E 831 | |
CTE, -40°C to 40°C, xflow | 6.66E-05 | 1/°C | ASTM E 831 | |
CTE, 23°C to 80°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 | |
CTE, 23°C to 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 | |
Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 141 | °C | ISO 306 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.2 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method | |
Melt Flow Rate, 300°C/1.2 kgf | 5.5 | g/10 min | ASTM D 1238 | |
Density | 1.2 | g/cm³ | ISO 1183 | |
Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 | |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
Melt Volume Rate, MVR at 300°C/1.2 kg | 5 | cm³/10 min | ISO 1133 |
Source GMD, last updated:2012/07/09 |
Processing |
Parameter | ||
Sheet Extrusion | Value | Unit |
Drying Temperature | 110 - 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 245 - 260 | °C |
Barrel - Zone 1 Temperature | 250 - 290 | °C |
Barrel - Zone 2 Temperature | 245 - 270 | °C |
Barrel - Zone 3 Temperature | 225 - 255 | °C |
Adapter Temperature | 225 - 255 | °C |
Die Temperature | 240 - 260 | °C |
Roll Stack Temp - Top | 75 - 115 | °C |
Roll Stack Temp - Middle | 80 - 125 | °C |
Roll Stack Temp - Bottom | 120 - 145 | °C |