TYPICAL PROPERTIES (1) |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min |
810 |
kgf/cm² |
ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min |
660 |
kgf/cm² |
ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min |
7 |
% |
ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min |
70 |
% |
ASTM D 638 |
Tensile Modulus, 50 mm/min |
29500 |
kgf/cm² |
ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
1220 |
kgf/cm² |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
26500 |
kgf/cm² |
ASTM D 790 |
Hardness, Rockwell L |
108 |
- |
ASTM D 785 |
Hardness, Rockwell M |
93 |
- |
ASTM D 785 |
Taber Abrasion, CS-17, 1 kg |
10 |
mg/1000cy |
ASTM D 1044 |
Taber Abrasion, CS-17, 1 kg |
10 |
mg/1000cy |
SABIC Method |
Tensile Stress, yield, 50 mm/min |
80 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
60 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
7 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
40 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2450 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
108 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2450 |
MPa |
ISO 178 |
Hardness, H358/30 |
128 |
MPa |
ISO 2039-1 |
Pencil Hardness test, 1kgf |
H |
- |
ASTM D 3363 |
Erichson scratch depth, 6N |
14 |
micrometer |
SABIC Method |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, unnotched, 23°C |
NB |
cm-kgf/cm |
ASTM D 4812 |
Izod Impact, notched, 23°C |
3 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched, -30°C |
3 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy, 23°C |
305 |
cm-kgf |
ASTM D 3763 |
Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C |
45 |
kJ/m² |
ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C |
5 |
kJ/m² |
ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C |
4 |
kJ/m² |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
3 |
kJ/m² |
ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
3 |
kJ/m² |
ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
47 |
kJ/m² |
ISO 179/1eU |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50 |
139 |
°C |
ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed |
133 |
°C |
ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed |
119 |
°C |
ASTM D 648 |
CTE, -40°C to 95°C, flow |
7.E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 95°C, xflow |
7.E-05 |
1/°C |
ASTM E 831 |
Specific Heat |
1.4 |
J/g-°C |
ASTM C 351 |
Thermal Conductivity |
0.2 |
W/m-°C |
ASTM C 177 |
Thermal Conductivity |
0.2 |
W/m-°C |
ISO 8302 |
CTE, 23°C to 80°C, flow |
7.E-05 |
1/°C |
ISO 11359-2 |
CTE, 23°C to 80°C, xflow |
7.E-05 |
1/°C |
ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 |
Ball Pressure Test, approximate maximum |
140 |
°C |
IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 |
138 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
140 |
°C |
ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
131 |
°C |
ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
118 |
°C |
ISO 75/Af |
PHYSICAL |
Value |
Unit |
Standard |
Specific Gravity |
1.2 |
- |
ASTM D 792 |
Specific Volume |
0.85 |
cm³/g |
ASTM D 792 |
Density |
1.17 |
g/cm³ |
ASTM D 792 |
Water Absorption, 24 hours |
0.08 |
% |
ASTM D 570 |
Water Absorption, equilibrium, 23C |
0.28 |
% |
ASTM D 570 |
Water Absorption, 50% RH, equilib |
0.13 |
% |
ASTM D 570 |
Moisture Absorption, 50% RH, 24 hrs |
0.04 |
% |
ASTM D 570 |
Mold Shrinkage, flow, 3.2 mm (5) |
0.5 - 0.8 |
% |
SABIC Method |
Melt Flow Rate, 300°C/1.2 kgf |
14.5 |
g/10 min |
ASTM D 1238 |
Density |
1.17 |
g/cm³ |
ISO 1183 |
Water Absorption, (23°C/sat) |
0.27 |
% |
ISO 62 |
Moisture Absorption (23°C / 50% RH) |
0.13 |
% |
ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg |
13 |
cm³/10 min |
ISO 1133 |
OPTICAL |
Value |
Unit |
Standard |
Light Transmission, 2.54 mm |
88 |
% |
ASTM D 1003 |
Haze, 2.54 mm |
<0.8 |
% |
ASTM D 1003 |
Refractive Index |
1.584 |
- |
ASTM D 542 |
Refractive Index |
1.584 |
- |
ISO 489 |
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
UL Recognized, 94HB Flame Class Rating (3) |
1 |
mm |
UL 94 |