TYPICAL PROPERTIES (1) |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min |
700 |
kgf/cm² |
ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min |
560 |
kgf/cm² |
ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min |
7 |
% |
ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min |
50 |
% |
ASTM D 638 |
Tensile Modulus, 5 mm/min |
26000 |
kgf/cm² |
ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
1120 |
kgf/cm² |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
25500 |
kgf/cm² |
ASTM D 790 |
Tensile Stress, yield, 50 mm/min |
73 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
55 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
7 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
>25 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2400 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
100 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2500 |
MPa |
ISO 178 |
Hardness, H358/30 |
110 |
MPa |
ISO 2039-1 |
Pencil Hardness test, 1kgf |
HB |
- |
ASTM D 3363 |
Erichson scratch depth, 6N |
17 |
micrometer |
SABIC Method |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, notched, 23°C |
1 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy, 23°C |
734 |
cm-kgf |
ASTM D 3763 |
Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C |
5 |
kJ/m² |
ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C |
3 |
kJ/m² |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
3 |
kJ/m² |
ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
5 |
kJ/m² |
ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
90 |
kJ/m² |
ISO 179/1eU |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50 |
137 |
°C |
ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed |
132 |
°C |
ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed |
121 |
°C |
ASTM D 648 |
CTE, -40°C to 95°C, flow |
7.E-05 |
1/°C |
ASTM E 831 |
CTE, -40°C to 95°C, xflow |
7.E-05 |
1/°C |
ASTM E 831 |
Thermal Conductivity |
0.2 |
W/m-°C |
ASTM C 177 |
Thermal Conductivity |
0.2 |
W/m-°C |
ISO 8302 |
CTE, 23°C to 80°C, flow |
7.E-05 |
1/°C |
ISO 11359-2 |
CTE, 23°C to 80°C, xflow |
7.E-05 |
1/°C |
ISO 11359-2 |
Vicat Softening Temp, Rate B/50 |
140 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
141 |
°C |
ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
133 |
°C |
ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
120 |
°C |
ISO 75/Af |
PHYSICAL |
Value |
Unit |
Standard |
Specific Gravity |
1.2 |
- |
ASTM D 792 |
Density |
1.19 |
g/cm³ |
ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm (5) |
0.6 - 0.8 |
% |
SABIC Method |
Mold Shrinkage, xflow, 3.2 mm (5) |
0.6 - 0.8 |
% |
SABIC Method |
Melt Flow Rate, 300°C/1.2 kgf |
38.5 |
g/10 min |
ASTM D 1238 |
Density |
1.19 |
g/cm³ |
ISO 1183 |
Melt Volume Rate, MVR at 300°C/1.2 kg |
36 |
cm³/10 min |
ISO 1133 |
OPTICAL |
Value |
Unit |
Standard |
Refractive Index |
1.586 |
- |
ASTM D 542 |
Refractive Index |
1.586 |
- |
ISO 489 |