SABIC Innovative Plastics LEXAN 920A PC (Americas) | |||
---|---|---|---|
Categories: | Polymer; Thermoplastic; Polycarbonate (PC) | ||
Material Notes: | Low viscosity injection moldable, flame retardant PC. Exceptional surface appearance. Clear, tints and opaque colors.
Information provided by SABIC Innovative Plastics for the Americas. |
||
|
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D 792 | ||
Density | 1.217 g/cc | 0.04397 lb/in³ | ASTM D 792 | ||
Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D 570 | ||
Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ASTM D 570 | ||
0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D 570 | |||
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
Melt Flow | 14.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
14.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell M | 70 | 70 | ASTM D 785 | ||
Hardness, Rockwell R | 118 | 118 | ASTM D 785 | ||
Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 | ||
Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 | ||
Elongation at Break | 90 % | 90 % | Type I, 50 mm/min; ASTM D 638 | ||
Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 | ||
Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | ||
Flexural Modulus | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | ||
Izod Impact, Notched | 6.40 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | ||
Izod Impact, Unnotched | 32.04 J/cm @Temperature 23.0 °C |
60.02 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 | ||
Tensile Impact Strength | 525 kJ/m² | 250 ft-lb/in² | Type S; ASTM D 1822 | ||
Falling Dart Impact | 169 J @Temperature 23.0 °C |
125 ft-lb @Temperature 73.4 °F |
ASTM D 3029 | ||
Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; ASTM D 1044 | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D 257 | ||
Dielectric Constant | 2.96 @Frequency 1.00e+6 Hz |
2.96 @Frequency 1.00e+6 Hz |
ASTM D 150 | ||
3.01 @Frequency 50.0 - 60.0 Hz |
3.01 @Frequency 50.0 - 60.0 Hz |
ASTM D 150 | |||
Dielectric Strength | 16.7 kV/mm @Thickness 3.20 mm |
424 kV/in @Thickness 0.126 in |
in air; ASTM D 149 | ||
Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D 150 | ||
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D 150 | |||
Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | PLC 7; ASTM D 495 | ||
Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2; UL 746A | ||
Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC 2; UL 746A | ||
High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | PLC 3; UL 746A | ||
High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3; UL 746A | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | ||
Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C 177 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | ||
Vicat Softening Point | 151 °C | 304 °F | Rate B/50; ASTM D 1525 | ||
UL RTI, Electrical | 130 °C | 266 °F | UL 746B | ||
UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B | ||
UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B | ||
Flammability, UL94 | V-2 @Thickness 1.47 mm |
V-2 @Thickness 0.0579 in |
UL 94 | ||
V-0 @Thickness 2.99 mm |
V-0 @Thickness 0.118 in |
UL 94 | |||
Optical Properties | Metric | English | Comments | ||
Refractive Index | 1.586 | 1.586 | ASTM D 542 | ||
Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 | ||
Transmission, Visible | 85 % | 85 % | ASTM D 1003 | ||
Descriptive Properties | |||||
Radiant Panel Listing | YES | UL Tested |