SABIC Innovative Plastics LEXAN FST9705 PC Copolymer (Americas) | |||
---|---|---|---|
Categories: | Polymer; Thermoplastic; Polycarbonate (PC) | ||
Material Notes: | High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin
Information provided by SABIC Innovative Plastics for the Americas. |
||
|
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D 792 | ||
Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
Moisture Absorption | 0.110 % @Temperature 23.0 °C |
0.110 % @Temperature 73.4 °F |
50% RH; ISO 62 | ||
Water Absorption at Saturation | 0.28 % @Temperature 23.0 °C |
0.28 % @Temperature 73.4 °F |
ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method | ||
Melt Flow | 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
cm^3/10 min Melt Volume Rate; ISO 1133 | ||
5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 | |||
16 g/10 min @Load 5.00 kg, Temperature 300 °C |
16 g/10 min @Load 11.0 lb, Temperature 572 °F |
cm^3/10 min Melt Volume Rate; ISO 1133 | |||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 | ||
76.0 MPa | 11000 psi | 50 mm/min; ISO 527 | |||
Tensile Strength, Yield | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D 638 | ||
74.0 MPa | 10700 psi | 50 mm/min; ISO 527 | |||
Elongation at Break | 102 % | 102 % | Type I, 50 mm/min; ASTM D 638 | ||
109 % | 109 % | 50 mm/min; ISO 527 | |||
Elongation at Yield | 6.7 % | 6.7 % | Type I, 50 mm/min; ASTM D 638 | ||
6.8 % | 6.8 % | 50 mm/min; ISO 527 | |||
Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 | ||
2.61 GPa | 379 ksi | 5 mm/min; ASTM D 638 | |||
Flexural Yield Strength | 107 MPa | 15500 psi | 2 mm/min; ISO 178 | ||
115 MPa | 16700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |||
Flexural Modulus | 2.32 GPa | 336 ksi | 2 mm/min; ISO 178 | ||
2.50 GPa | 363 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |||
Izod Impact, Notched | 1.12 J/cm @Temperature -30.0 °C |
2.10 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | ||
1.94 J/cm @Temperature 23.0 °C |
3.63 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |||
Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | ||
16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |||
Charpy Impact, Notched | 2.40 J/cm² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
Impact Test | 80.0 J @Temperature 23.0 °C |
59.0 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 57.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
57.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |||
CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |||
Hot Ball Pressure Test | <= 125 °C | <= 257 °F | IEC 60695-10-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |||
Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ISO 306 | ||
139 °C | 282 °F | Rate B/120; ISO 306 | |||
140 °C | 284 °F | Rate B/50; ASTM D 1525 | |||
Descriptive Properties | |||||
NBS Smoke Density, Flaming, Dmax | <25 | ASTM E 662 | |||
OSU total heat release; 2 min. (kW-min/m^2) | <55 | FAR 25.853 | |||
OSU peak heat release rate, 5 min. (kW/m^2) | <55 | FAR 25.853 | |||
Vertical Burn a (60s) passes at (sec) | 2.4 | FAR 25.853 | |||
Vertical Burn b (12s) passes at (sec) | 0.5 | FAR 25.853 |