SABIC Innovative Plastics LEXAN FST3403 PC Copolymer (Americas)
Categories:	Polymer; Thermoplastic; Polycarbonate (PC)
Material Notes:	LEXAN FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior applications (category R6). It also meets requirements of DIN5510-2, NFPA-130 and PN-K-02511 standards. Available in opaque colors. Information provided by SABIC Innovative Plastics for the Americas.
Add to Folder:  t name="ctl00$ContentMain$ucDataSheet1$drpFolderList" style="font-size: 8pt;">  My Folder    nly="readonly" value="0/0" style="font-size: 10pt; border: 0px none white; color: black; width: 35px; font-weight: bold; background-color: inherit;" />

Physical Properties	Metric	English	Comments
Specific Gravity	1.33 g/cc	1.33 g/cc	ASTM D 792
Density	1.33 g/cc	0.0480 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	SABIC Method
Melt Flow	10 g/10 min @Load 1.20 kg, Temperature 300 °C	10 g/10 min @Load 2.65 lb, Temperature 572 °F	cm^3/10 min Melt Volume Rate; ISO 1133
	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D 1238
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa	10200 psi	50 mm/min; ISO 527
	70.0 MPa	10200 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	77.0 MPa	11200 psi	50 mm/min; ISO 527
	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	80 %	80 %	50 mm/min; ISO 527
	80 %	80 %	Type I, 50 mm/min; ASTM D 638
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ISO 527
	6.0 %	6.0 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	2.60 GPa	377 ksi	1 mm/min; ISO 527
	2.60 GPa	377 ksi	5 mm/min; ASTM D 638
Flexural Yield Strength	110 MPa	16000 psi	2 mm/min; ISO 178
	115 MPa	16700 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	2.50 GPa	363 ksi	1.3 mm/min, 50 mm span; ASTM D 790
	2.70 GPa	392 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.900 J/cm @Temperature -30.0 °C	1.69 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	1.30 J/cm @Temperature 23.0 °C	2.44 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	80*10*3; ISO 180/1A
	10.0 kJ/m² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	80*10*4; ISO 180/1A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	80*10*4; ISO 180/1A
	13.0 kJ/m² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80*10*3; ISO 180/1U
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	80*10*3; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80*10*4; ISO 180/1U
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	80*10*4; ISO 180/1U
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80*10*4 sp=62mm; ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test	125 J	92.2 ft-lb	Multiaxial Impact; ISO 6603
	80.0 J @Temperature 23.0 °C	59.0 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	105 °C	221 °F	Flatw 80*10*4 sp=64mm; ISO 75/Bf
	104 °C @Thickness 3.20 mm	219 °F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	95.0 °C	203 °F	Flatw 80*10*4 sp=64mm; ISO 75/Af
	93.0 °C @Thickness 3.20 mm	199 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	114 °C	237 °F	Rate B/50; ASTM D 1525
	114 °C	237 °F	Rate B/50; ISO 306
	115 °C	239 °F	Rate B/120; ISO 306
Descriptive Properties
Fire Safety Hazard Level - Requirement set R6	HL3		EN 45545-2:2013
Heat release, MAHRE, 50 kW/m2, 3 mm	<60 kW/m^2		ISO 5660-1
Smoke density, DS-4, 50 kW/m2, 3mm	<150		ISO 5659-2
Smoke density, VOF4, 50 kW/m2, 3mm	<300		ISO 5659-2
Smoke toxicity, CITG (8 min), 50 kW/m2, 3 mm	0.1		ISO 5659-2