SABIC Innovative Plastics LEXAN 925 PC (Americas) | |||
---|---|---|---|
Categories: | Polymer; Thermoplastic; Polycarbonate (PC) | ||
Material Notes: | LEXAN 925 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has a UL V0 rating. LEXAN resin 925 is available in various opaque color options and is a general-purpose resin that is an excellent candidate for a wide variety of applications.
Information provided by SABIC Innovative Plastics for the Americas. |
||
Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 14 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
Elongation at Break | 125 % | 125 % | Type I, 50 mm/min; ASTM D 638 |
Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
Tensile Modulus | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D 638 |
Flexural Yield Strength | 101 MPa | 14600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
Impact Test | 73.0 J @Temperature 23.0 °C |
53.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
Electrical Properties | Metric | English | Comments |
Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | PLC 7; ASTM D 495 |
Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2; UL 746A |
Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC 2; UL 746A |
High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | PLC 3; UL 746A |
High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC 4; UL 746A |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
CTE, linear, Transverse to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ASTM D 1525 |
UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
UL 94 |
V-0 @Thickness 1.10 mm |
V-0 @Thickness 0.0433 in |
UL 94 | |
Glow Wire Test | 800 °C @Thickness 1.00 mm |
1470 °F @Thickness 0.0394 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
Glow Wire Flammability Index; IEC 60695-2-12 |